317L is a molybdenum bearing, low carbon content "L" grade austenitic stainless steel that provides improved corrosion resistance to 304L and 316L stainless steels. Low carbon provides sensitizing resistance during welding and other heat treatments. 317L is non-magnetic under annealed conditions, but may become slightly magnetic due to welding.
| Specifications | ASTM A 276/A 276M,A 484/A 484M,A 564/A 564M,A 582/A582M,A 638 /A 638M,A705/A705M |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| SS 317 Angle | 5mm to 9mm |
| Thickness | 3.0mm – 120mm |
| Length | 3MTR, 4MTR, 5MTR, 6MTR, or Custom Cut Sizes |
| Type | Angle, C Channel, U Channel, H Beam, I Beam, T Beam, W Beam, Chain |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 317L | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 18.00 - 20.00 | 3.00 - 4.00 | 11.00 - 15.00 | 57.845 min |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.9 g/cm3 | 1400 °C (2550 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35% |
317L is a molybdenum bearing, low carbon content "L" grade austenitic stainless steel that provides improved corrosion resistance to 304L and 316L stainless steels. Low carbon provides sensitizing resistance during welding and other heat treatments. 317L is non-magnetic under annealed conditions, but may become slightly magnetic due to welding.
| Specifications | ASTM A 276/A 276M,A 484/A 484M,A 564/A 564M,A 582/A582M,A 638 /A 638M,A705/A705M |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| SS 317 Angle | 5mm to 9mm |
| Thickness | 3.0mm – 120mm |
| Length | 3MTR, 4MTR, 5MTR, 6MTR, or Custom Cut Sizes |
| Type | Angle, C Channel, U Channel, H Beam, I Beam, T Beam, W Beam, Chain |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 317L | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 18.00 - 20.00 | 3.00 - 4.00 | 11.00 - 15.00 | 57.845 min |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.9 g/cm3 | 1400 °C (2550 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35% |