Type 310s is an austenitic chromium-nickel stainless steel (maximum carbon content of 0.08%) with good oxidation resistance and strength at high temperatures. It can resist oxidation in continuous service up to 2000oF as long as reducing sulfur gases are not present. It can also be used in intermittent service at temperatures up to 1900oF because it resists recalcification and has a low coefficient of expansion. This factor reduces the tendency of the steel to warp in hot service. 310s is similar to 310, except that the carbon content is lower to reduce carbide precipitation during welding.
1) Hot rolled flat steel: (3-30)*(10-200mm)*6000mm or as per your requirement.
2) Cold-drawn flat steel: (3-30)*(10-200mm)*6000mm or according to your requirement
Product Name | 310S Stainless Steel Bar | |
Grade | 200, 300, 400series, etc | |
Surface | Bright, Polished, Turn smooth(Peeled), Brush, Mill, Pickled, etc | |
Type | Round, Square, Hexagonal, Flat, Angle | |
Specification | Round bar | Diameter: 3mm~800mm |
Hexagonal | Size: 2mm~100mm | |
Square bar | Size: 4mm*4mm~100mm*100mm | |
Flat bar | Thickness: 2mm~100mm, Width: 10mm~500mm | |
Angle bar | Size: 3mm*20mm*20mm~12mm*100mm*100mm | |
Standard | AISI, ASTM, DIN, GB, JIS, SUS, ASTM A276, A484, A479, A580, A582, JIS G4303, JIS G4311, DIN 1654-5, DIN 17440, GB/T 1220 | |
Treatment | Hot rolled, Cold drawn, Annealed, Grinding | |
Trade Terms | EXW, FOB, CFR, CIF | |
Stainless steels are known as high-alloy steels. They are classified into ferritic, austenitic, and martensitic steels based on their crystalline structure.
Grade 310S stainless steel is superior than 304 or 309 stainless steel in most environments, because it has high nickel and chromium content. It has high corrosion resistance and strength in temperatures up to 1149°C (2100°F).
310S stainless steel has good high temperature resistance. When the temperature exceeds 800 [1], it begins to soften, the allowable stress begins to continue to decrease, and the maximum service temperature is 1200°C. Due to the high content of nickel (Ni) and chromium (Cr), it has good oxidation resistance, corrosion resistance, acid and alkali resistance, and high temperature resistance. High temperature resistant steel pipes are specially used to manufacture electric furnace tubes. The austenitic stainless steel adds carbon After the content, the strength is improved due to its solid solution strengthening effect. The chemical composition of austenitic stainless steel is based on chromium and nickel with the addition of elements such as molybdenum, tungsten, niobium, and titanium. Because of its face-centered cubic structure, Therefore, it has high strength and creep strength at high temperature.
| Grade | Cr | Ni | C | Si | Mn | P | S | Mo | Cu | Fe |
| 310S | min: 24.0 | min: 19.0 | 0.08 | 1 | 2 | 0.045 | 0.03 | 0.75 | 0.5 | balance |
| max: 26.0 | max: 22.0 |
| Grade | Tensile Strength ksi (min.) | Yield Strength 0.2% Offset ksi (min.) | Elongation - % in 50 mm (min.) | Hardness (Brinell) MAX | Hardness (Rockwell B) MAX |
| 310S | 75 | 30 | 40 | 217 | 95 |
Type 310s is an austenitic chromium-nickel stainless steel (maximum carbon content of 0.08%) with good oxidation resistance and strength at high temperatures. It can resist oxidation in continuous service up to 2000oF as long as reducing sulfur gases are not present. It can also be used in intermittent service at temperatures up to 1900oF because it resists recalcification and has a low coefficient of expansion. This factor reduces the tendency of the steel to warp in hot service. 310s is similar to 310, except that the carbon content is lower to reduce carbide precipitation during welding.
1) Hot rolled flat steel: (3-30)*(10-200mm)*6000mm or as per your requirement.
2) Cold-drawn flat steel: (3-30)*(10-200mm)*6000mm or according to your requirement
Product Name | 310S Stainless Steel Bar | |
Grade | 200, 300, 400series, etc | |
Surface | Bright, Polished, Turn smooth(Peeled), Brush, Mill, Pickled, etc | |
Type | Round, Square, Hexagonal, Flat, Angle | |
Specification | Round bar | Diameter: 3mm~800mm |
Hexagonal | Size: 2mm~100mm | |
Square bar | Size: 4mm*4mm~100mm*100mm | |
Flat bar | Thickness: 2mm~100mm, Width: 10mm~500mm | |
Angle bar | Size: 3mm*20mm*20mm~12mm*100mm*100mm | |
Standard | AISI, ASTM, DIN, GB, JIS, SUS, ASTM A276, A484, A479, A580, A582, JIS G4303, JIS G4311, DIN 1654-5, DIN 17440, GB/T 1220 | |
Treatment | Hot rolled, Cold drawn, Annealed, Grinding | |
Trade Terms | EXW, FOB, CFR, CIF | |
Stainless steels are known as high-alloy steels. They are classified into ferritic, austenitic, and martensitic steels based on their crystalline structure.
Grade 310S stainless steel is superior than 304 or 309 stainless steel in most environments, because it has high nickel and chromium content. It has high corrosion resistance and strength in temperatures up to 1149°C (2100°F).
310S stainless steel has good high temperature resistance. When the temperature exceeds 800 [1], it begins to soften, the allowable stress begins to continue to decrease, and the maximum service temperature is 1200°C. Due to the high content of nickel (Ni) and chromium (Cr), it has good oxidation resistance, corrosion resistance, acid and alkali resistance, and high temperature resistance. High temperature resistant steel pipes are specially used to manufacture electric furnace tubes. The austenitic stainless steel adds carbon After the content, the strength is improved due to its solid solution strengthening effect. The chemical composition of austenitic stainless steel is based on chromium and nickel with the addition of elements such as molybdenum, tungsten, niobium, and titanium. Because of its face-centered cubic structure, Therefore, it has high strength and creep strength at high temperature.
| Grade | Cr | Ni | C | Si | Mn | P | S | Mo | Cu | Fe |
| 310S | min: 24.0 | min: 19.0 | 0.08 | 1 | 2 | 0.045 | 0.03 | 0.75 | 0.5 | balance |
| max: 26.0 | max: 22.0 |
| Grade | Tensile Strength ksi (min.) | Yield Strength 0.2% Offset ksi (min.) | Elongation - % in 50 mm (min.) | Hardness (Brinell) MAX | Hardness (Rockwell B) MAX |
| 310S | 75 | 30 | 40 | 217 | 95 |